Loctite SPD H3000 Cream Acrylic Adhesive in 5 Gallon Pails - Part A & B

Loctite SPD H3000 Cream Acrylic Adhesive in 5 Gallon Pails Overview

Loctite SPD H3000 is a general-purpose, 2-part, room-temperature curing acrylic adhesive paste with a precise 1:1 mix ratio for reliable and consistent results. Supplied in separate Part A (Resin) and Part B (Hardener) bulk 5-gallon pails, this resilient adhesive forms tough, impact-resistant bonds while maintaining strength over a wide temperature range. Tolerant of off-ratio mixing, it requires minimal surface preparation and is perfect for industrial applications bonding PVC, polycarbonate, acrylic, ABS, stainless steel, and FRP. With excellent environmental resistance, SPD H3000 ensures durable, high-performance results.

Bulk SPD H3000 Features and Benefits

• 5-Gallon Pail Format: Designed for high-volume industrial applications.
  
• 1:1 Mix Ratio: Ensures accurate, consistent results for every use.
  
• General-Purpose Structural Bonder: Provides exceptional impact, peel, and shear strength.
  
• Non-Sagging Paste: Fills gaps up to 0.375" (9.52 mm) without sagging.
  
• Minimal Surface Preparation: Reduces time and labor requirements.
  
• Rapid Cure: Cures quickly at room temperature with a 100% reactive formula.
  
• Excellent Environmental Resistance: Durable in harsh conditions.

Specifications

• Series: Loctite SPD H3000
  
• Type: Methacrylate Adhesive (MMA)
  
• Components: Two Components
  
• Application: Bonding
  
• Substrates: PVC, Polycarbonate, Acrylic, ABS, Stainless Steel, FRP
  
• Color (Mixed): Cream
  
• Package Size: 5 Gallon Pail
  
• Mix Ratio by Volume: 1:1
  
• Cure: Room Temperature
  
• Specific Gravity: 1.07
  
• Fixture Time: 12 to 15 Minutes
  
• Open Time: 4 to 6 Minutes
  
• Tensile Strength: 4,100 to 4,300 psi
  
• Elongation: 20 to 30%
  
• Shear Strength: 1,490 to 4,000 psi - Depending on Substrate
  
• Storage Temperature: 35°F to 45°F (1.6°C to 7.2°C)

Note: All results are based on testing at 70°F (21.1°C), unless stated otherwise.